Fabrication of Transparent Nanohybrids with Heat Resistance Using High-Density Amorphous Formation and Uniform Dispersion of Nanodiamond

A new technology for the production of transparent material using a “crystalline” polymer is proposed in the present study. Further, transparent and flexible crystalline polymer nanohybrid film containing well-dispersed nanodiamond filler was fabricated. Partially fluorinated crystalline polymer with switchboard-type lamellae results in high transparency as a consequence of the formation of a high-density amorphous structure based on high-temperature drawing just below the melting point at 110 °C. Although the formation of nanohybrid materials composed of fluorinated-polymer/organo-modified nanocarbon is generally difficult, we confirmed the formation, via melt-compounding, using atomic force microscopy and wide-angle X-ray diffraction. Even though the polymer matrix/nanodiamond hybrid has remarkable aggregation properties, a well-dispersed state was achieved because of improvement in wettability obtained through surface modification of filler.